The Effect of Curing Time and Light Intensity on Composite Resin: the Effect of Curing Time and Light Intensity on the Degree of Conversion of Poly-acid Modified Composite Resin M. G. Al-shaekh
Pedido desde almacén remoto
Los regalos de Navidad se podrán canjear hasta el 31 de enero
Nuestros clientes opinan:
The Effect of Curing Time and Light Intensity on Composite Resin: the Effect of Curing Time and Light Intensity on the Degree of Conversion of Poly-acid Modified Composite Resin
M. G. Al-shaekh
The aims of this study are to investigate the effect of light intensity and curing time on the degree of conversion and amount of residual monomer released from poly-acid modified composite resin samples cured with QTH light curing unit. Single light cured poly-acid modified composite resin restorative material Glasiosite Caps (VOCO/ Cuxhaven, Germany) (n=130 samples divided to the groups ) exposed to different exposure times (10, 30 and 40 seconds) and at different light intensities (410 and 490 mw/cm²). The degree of conversion of poly-acid modified composite resin samples was investigated by Fourier transform infrared spectroscopy (FTIR). While the amount of residual monomer released from poly-acid modified composite resin samples was investigated through measuring the released residual monomer in doubled distilled water with (CECIL 2000) Ultraviolet visible spectrophotometer.
| Medios de comunicación | Libros Paperback Book (Libro con tapa blanda y lomo encolado) |
| Publicado | 4 de marzo de 2011 |
| ISBN13 | 9783844310009 |
| Editores | LAP LAMBERT Academic Publishing |
| Páginas | 128 |
| Dimensiones | 226 × 8 × 150 mm · 209 g |
| Lengua | Alemán |